SINT-E10 Sinterstahl Cu-haltig (Copper-Bearing Sintered Steel)

SINT-E10 is an extra-high-density copper-bearing sintered steel structural material per DIN 30910-4. Maximum strength for demanding structural applications requiring superior load capacity.

Chemical Composition (per DIN 30910-4 (Sintered Metals for Structural Parts))

Element	Content
Fe	Rest (Balance)
C	< 0.3%
Cu	1–5%
Other	< 2%

Properties (per DIN 30910-4 (Sintered Metals for Structural Parts))

Property	Value
Density	> 7.2 g/cm³
Hardness HB	> 80
Tensile Strength Rm	340 N/mm²
Yield Strength Rp0.1	240 N/mm²
Elongation A	5%
E-Modulus	160 × 10³ N/mm²

Comparable Standards: MPIF FC-0200-K50. Tensile strength and yield strength values are for as-sintered condition unless otherwise specified.

Standard

Material Code

Density (g/cm3)

Hardness

Tensile Strength

Compositions (%)

Ultimate (MPa)

Yield (MPa)

Fe

Cu

C

Ni

Mo

Mn

Cr

Sn

DIN 30910-4:2004-05

Sint-E 10

>7.2

>HRB 80

340

240

Bal.

1.5