SINT-C01 Sintereisen C-haltig (Carbon-Bearing Sintered Iron)

SINT-C01 is a medium-density carbon-bearing sintered iron structural material per DIN 30910-4. Carbon addition significantly increases strength and hardness for structural applications requiring higher load capacity.

Chemical Composition (per DIN 30910-4 (Sintered Metals for Structural Parts))

Element	Content
Fe	Rest (Balance)
C	0.3–0.9%
Cu	< 1%
Other	< 2%

Properties (per DIN 30910-4 (Sintered Metals for Structural Parts))

Property	Value
Density	6.4–6.8 g/cm³
Hardness HB	> 70
Tensile Strength Rm	240 N/mm²
Yield Strength Rp0.1	170 N/mm²
Elongation A	2%
E-Modulus	100 × 10³ N/mm²

Comparable Standards: MPIF F-0005-K35 / ISO 5755 P1053Z. Tensile strength and yield strength values are for as-sintered condition unless otherwise specified.

Standard

Material Code

Density (g/cm3)

Hardness

Tensile Strength

Compositions (%)

Ultimate (MPa)

Yield (MPa)

Fe

Cu

C

Ni

Mo

Mn

Cr

Sn

DIN 30910-4:2004-05

Sint-C 01

6.4-6.8

>HRB 70

240

170

Bal.

0.5