SINT-C10 Sinterstahl Cu-haltig (Copper-Bearing Sintered Steel)

SINT-C10 is a medium-density copper-bearing sintered steel structural material per DIN 30910-4. Copper addition enhances strength and dimensional stability for structural parts requiring moderate load capacity.

Chemical Composition (per DIN 30910-4 (Sintered Metals for Structural Parts))

Element	Content
Fe	Rest (Balance)
C	< 0.3%
Cu	1–5%
Other	< 2%

Properties (per DIN 30910-4 (Sintered Metals for Structural Parts))

Property	Value
Density	6.4–6.8 g/cm³
Hardness HB	> 40
Tensile Strength Rm	200 N/mm²
Yield Strength Rp0.1	140 N/mm²
Elongation A	2%
E-Modulus	100 × 10³ N/mm²

Comparable Standards: MPIF FC-0200-K29 / ISO 5755 P2013Z. Tensile strength and yield strength values are for as-sintered condition unless otherwise specified.

Standard

Material Code

Density (g/cm3)

Hardness

Tensile Strength

Compositions (%)

Ultimate (MPa)

Yield (MPa)

Fe

Cu

C

Ni

Mo

Mn

Cr

Sn

DIN 30910-4:2004-05

Sint-C 10

6.4-6.8

>HRB 40

200

140

Bal.

1.5